Alusong Signage- Glossy

Colors & Surfaces

ALUSONG Glossy coating, with polyurethane as base and fluoride polymer as top coating, has good feature of weather resistance of 10 years for interiors use. Different from Polyester coating, it guarantees fresher, vivid color and higher gloss level, provide more choice for designer. It is available in colors that are not feasible with other coating system.

Color Silver Metallic

Product Ranges

Aluminum	AA1100 AA3003
Aluminum skin	0.15mm,0.21mm,0.30mm,0.35mm,0.40mm,0.45mm,0.5mm
Panel thickness	2mm, 3mm,4mm,5mm,6mm
Panel width	1220mm,1250mm,1500mm
Panel length	2440mm,3050mm,4050mm
Surface treatment	Glossy Polyester
Colors	70 colors, special colors available upon request
Customers size	accepted
Glossy	20%-80%

Dimensional tolerance:

Panel width: ±2mm Panel length:±3mm

Panel thickness: ±0.2mm Panel diagonal: ≤5mm

Aluminum sheet thickness: ±0.01mm

Product properties

Vivid colors

High resistance to peeling

Superior weather resistance

Light weight and easy to process

Coating evenness

Diversified colors

Easy for maintenance

Impact resistance

APPLICATIONS

· Sign Making, Shop Front

· Furniture &cabinets

· Standoff Lettering

· Interior decoration

· Cladding&facade

· Modular Sign Systems

· Exhibition Design

Application
Application
Application
Application
Application

Technical Data

Description	Test standard	Polyester
Thickness of coating	Polyester paint >=16um	16um to 18um
Coating flexibility (T-bend)	Polyester paint≥3T	3T
Color different	ΔE≦2.0(follow color sample)	ΔE≦2.0
Pencil hardness	≧HB	≧2H
Chemical resistance	2%HCI or 2%NaOH test in 24 hours -No change	No change
Coating adhesion	≧1grade for 10810mm2gridding test	1grade
Resist solvent	100times with Dimethylebnzene without change	No change
Boiling water resistance	2 hours without change	No change
Peeling strength/stripping strength	Average ≧5N/mm of 180oc peel off for panel with 0.21mm alu.skin	5N/mm
Impact test for paint	20KG.cm impact-paint no split for panel	No split
Abrasion resistance (L/Mil)	NIL	NIL
Temperature resistance	-40℃ to +80℃ temperature without change of color difference and paint peel off,peeling strength average dropprate≦10%	Change of glossy only,no paint Peel off
Cofficient of linear Thermal Expansion	100℃ temperature difference	2.4mm/n
Detergent resistance (3%)	ASTM D2248	No change
Humidity Resistance (3000hrs,100%RH,100°F)	ASTM D2247	No change
Salt spray resistance (3000hrs,5% salt)	ASTM B117	No change
Resistance to Staining	600h radiate in 800W/M2 in humidity condition,glossiness deviation less grade 2,color difference ≦4.0	No change